STUDY ON PREPARATION AND PHYSICAL PROPERTIES OF Fe2O3 NANOPOWDERS
Fe2O3 nanopowders were prepared by solid phase reaction method.The phase structure,microstructure,magnetic properties and gas sensor properties were characterized by X-ray diffraction (XRD),scanning electron microscope (SEM),vibration sample magnetometer (VSM) and gas sensor measuring system.It was found that the precursor sintered at 300 ℃ was spinel structure and transformed into α-Fe2O3 above 400 ℃.The results of the room temperature hysteresis loops showed that the results obtained from the magnetic hystersis loop at room temperature were in agreement with those from the XRD spectra.Moreover,it was shown that γ-Fe2O3 can be used as gas sensor of the alcohol.he α-Fe2O3 nanopowders can be obtained at a lower sintering temperature.In addition,the gas sensor ofγ-Fe2O3 was more sensitive to the alcohol.
Dry gel Thermal analysis Gas sensor properties Spinel structure
Ying-ming SHEN Jie HU Bian-fang ZHANG Xue-qian FANG
Department of Science and Technology, Shijiazhuang Tiedao University, Shijiazhuang, 050043, China School of Continuing Education, Shijiazhuang Tiedao University, Shijiazhuang, 050043, China Department of Mathematics and Physics, Shijiazhuang Tiedao University, Shijiazhuang, 050043, China Department of Engineering Mechanics, Shijiazhuang Tiedao University, Shijiazhuang, 050043, China
国际会议
石家庄
英文
473-476
2019-11-01（万方平台首次上网日期，不代表论文的发表时间）