A primary study on tensile strength stability of Mg-5Y-3Sm-0.5Sb alloy

摘要：

　　The tensile strength stability of aging hardened Mg-5Y-3Sm-0.5Sb alloy was primarily studied.The results showed that the alloy has good tensile strength at room and high temperature.The tensile strength decreases slowly from 258 MPa at room temperature to 195 MPa at 300 ℃.The tensile strength stability is superior to that of commercial heat resistant magnesium alloy WE54 developed most successfully.The formation of Mg24Y5 phase is observed in the alloy.The tensile strength of the alloy keeps a linear relationship with the hardness of strengthening phase Mg24Y5.The reason for the tensile strength stability is mainly attributed to the hardness stability of Mg24Y5 phase in the alloy.

关键词： magnesium alloy microstructure tensile strength strengthening phase

作者: Qing Zhang Jun Chen Quan-an Li

作者单位: School of Materials Science and Engineering,Henan University of Science and Technology,Luoyang,China;Collaborative Innovation Center of Nonferrous Metals,Henan Province,Luoyang,China

会议类型: 国际会议

会议名称: 2017 6th International Conference on Advanced Materials and Computer Science (ICAMCS 2017) 2017年第六届先进材料与计算机科学国际会议(ICAMCS 2017)

会议地点: 郑州

会议语种:英文

页码: 1-5

在线出版日期: 2017-04-29（万方平台首次上网日期，不代表论文的发表时间）