Influence of pre-deformation on the precipitation of Cu-rich clusters in RPV model steel
The effect of pre-deformation on the precipitation process of Cu-rich clusters in reactor pressure vessels(RPV)model steel is studied.In this research,Fe-1.16wt%Cu binary alloy is selected as RPV model steel to simulate the precipitation process of Cu-rich clusters.The solid-solution Fe-Cu alloys were cold rolled with pre-deformation of 0,10%,25%,40%,60%,followed by aging at 450 ℃ for a series time.The dislocation density,Vickers hardness and microstructure evolution of Fe-Cu alloys after aging were determined.It is revealed that the Vickers hardness of un-deformed specimens reaches to peak hardness after aging at 450 ℃ for 100 h,while the specimens with larger dislocation density reach to peak hardness faster from the Vickers hardness test result.The result of transmission electron microscopy(TEM)indicates that pre-deformation promotes the process of precipitation of Cu-rich clusters and inhibits the growth of the Cu-rich clusters.
Zhaozhao Tan Chengliang Li Guogang Shu Wei Liu Qiulin Li
Graduate School at Shenzhen,Tsinghua University,518055 Shenzhen,Guangdong,China China Nuclear Power Engineering Co.,Ltd.,518031 Shenzhen,Guangdong,China Sate Key Laboratory of Nuclear Power Safety Monitoring Technology and Equipment,China Nuclear Power School of Material Science and Engineering,Tsinghua university,100084 Beijing,China
国际会议
广州
英文
1-5
2018-05-11（万方平台首次上网日期，不代表论文的发表时间）