THE STUDY ON THE PREPARATION AND PROPERTIES OF TRFC

摘要：

　　In this paper,thermoplastic fiberglass textile was embedded into the foamed cement matrix.Thermoplastic glass fiber textile reinforced cement-based foamed composites(TRFC)was prepared and modeled.The influence of glass textile on compressive strength,thermal conductivity,water absorption,drying shrinkage and flexural properties of textile reinforced composites were studied,and the mechanism of improvement was also analyzed.Compared to ordinary cement-based foamed plate,a consistent result can be obtained in two different apparent densities of(220-250)kg/m3 and(260-300)kg/m3.Compressive strength was obviously improved.Thermal conductivity increases a bit,but the composites still have a good thermal insulation property.The water absorption increased slightly,but drying shrinkage reduces.And flexural strength increased significantly,the maximum reached 0.67MPa and 0.9MPa,increased by 6.7 times and 7.5 times respectively.

关键词： TRFC textile cement-based foamed plate thermal conductivity flexural strength

作者: Jiujun Yang Yuling Zhou Lei Zhang

作者单位: College of Materials Science and Engineering,Tianjin Chengjian University,Tianjin 300384,China;Key L College of Materials Science and Engineering,Tianjin Chengjian University,Tianjin 300384,China

会议类型: 国际会议

会议名称: 2016 International Symposium on Civil and Environmental Engineering(2016年土木与环境工程国际研讨会)

会议地点: 武汉

会议语种:英文

页码: 87-91

在线出版日期: 2016-12-20（万方平台首次上网日期，不代表论文的发表时间）