Warm Stamping Technology of the Medium-Mn Steel

  The microstructure and mechanical of 22MnB5 steel,Al-Si coated 22MnB5 steel,and medium-Mn steel are studied before and after hot/warm stamping process.The results show that the austenite temperature is 800℃ for medium-Mn steel to obtain the tensile strength of 1500MPa,which is much lower than that of 22MnB5 steel (950℃),medium-Mn steel obtain finer microstructure and no surface decarburization without protective atmosphere,the total elongation reaches 10%,which is higher than that of 22MnB5 steel (7.5% ).

medium-Mn steel warm stamping hot stamping martensite

WANG Cunyu CHANG Ying ZHAO Shihao CAO Wenquan DONG Han WANG Yide

Central Iron and Steel Research Institute, Beijing 100081, China;Taiyuan Iron and Steel(Group)Co., L National Key Laboratory of Industrial Equipment Structural Analysis, School of Automotive Engineerin Central Iron and Steel Research Institute, Beijing 100081, China Taiyuan Iron and Steel(Group)Co., Ltd., Taiyuan 030003, Shanxi, China

国际会议

the 1st International Conference on Automobile Steel & The 3rd International Conference on High Manganese Steels (第一届国际汽车用钢大会暨第三届高锰钢国际会议)

成都

英文

225-228

2016-11-16(万方平台首次上网日期,不代表论文的发表时间)