Microstructure of Sm-Fe films electrodeposited in a high static magnetic field

摘要：

　　Sm-Fe alloy films were electrodeposited in a high static magnetic field with the magnetic flux is perpendicular to the electric current.The samples were prepared on Cu substance in an aqueous solution by constant voltage method.The magnetic flux density used in the experiments were 0 T,2 T and 4 T,respectively.The microstructures,preferential orientation,composition of samples were characterized by SEM(equipped with EDS),AFM and XRD,respectively.The results showed that the thickness of films increased,whereas the concentration of Sm in films ascended first and then descended with the increasing of the flux density.The crystal grains were coarsened under the magnetic fields.The morphology of grains changed from granular at 0 T,to rough at 2 T and to cauliflower like at 4 T.The AFM results confirmed the different roughness of samples.However,the external field has not influenced the orientation of samples significantly.

关键词： Sm-Fe film electrodeposition high magnetic filed microstructure

作者: LOU Chang-sheng KOU Ying ZHANG Wei-qiang

作者单位: School of Materials Science and Engineering,Shenyang Ligong University,Shenyang 110159,Liaoning,China

会议类型: 国际会议

会议名称: The 7th International Conference on Electromagnetic Processing of Materials(第七届冶金与材料电磁过程国际大会)

会议地点: 北京

会议语种:英文

页码: 1-4

在线出版日期: 2012-10-22（万方平台首次上网日期，不代表论文的发表时间）