Corrosion and soldering behaviour of STD61 coated by Arc Ion Plating coatings
In order to investigate corrosion and soldering behaviour of STD61, TiN and TiAIN were coated on the surface of STD61 by using Arc Ion Plating.The structure of the coatings was examined as a function of deposition conditions by X-ray diffraction, and the crystallographic orientation was determined by use of a texture coefficient.TiN coating was grown with a strong (111) preferred orientation of a typical NaCl-type crystal structure.This strong (111) preferred orientation had been commonly observed from the TiN coatings deposited by physical vapour deposition techniques.TiAIN coatings, however, showed relatively multiple orientations mainly of (111) and (200).Furthermore, TiAIN film demonstrated superior corrosion resistance in a molten aluminum alloy at 680C.This paper described in detail the corrosion and mass loss phenomena related to this steel-cast metal interaction.
Arc Ion Plating Corrosion Soldering STD61 Aluminum
S.W.Choi Y.C.Kim C.W.Kim J.I.Cho C.S.Kang
KITECH,6 Cheomdan-gwagiro 208 beon-gil,Buk-gu,Gwangju 500-480,Republic of Korea
国际会议
香港
英文
39-42
2013-06-25（万方平台首次上网日期，不代表论文的发表时间）