Effects of Al2O3 coating on the structural and electrochemical performance of LiNi0.5Co0.2Mn0.3O2 cathode material
The pristine LiNi0.5Co0.2Mn0.3O2 cathode material particles were successfully coated with Al2O3 via a heterogeneous nucleation process and subsequent heat-treatment.The structure and electrochemical properties of Al2O3-coated LiNi0.5Co0.2Mn0.3O2 were characterized by XRD and constant-current charge/discharge cycling tests.It was found that the Al2O3 coating did not alter the crystal structure of the cathode material.The Al2O3 coating layer had a negative influence on the dicharge specific capacity and a positive effect on the cycling performance.The decreased discharge capacity of the coated sample can be attributed to the poor clectronic and ionic conductivity of Al2O3 layer, which interfered the Li+ intercaltion/deintercaltion into/from the cathode material.The enhanced cycling performance can be ascribed to the suppression of the dissolution of transition metal ions by the HF acid in the eletrolyte and the side reations between electrode and electrolyte by the Al2O3 coating layer.The 2wt.% Al2O3-coated sample exhibits the optimal overall electrochemical performance, with discharge specific capacities of 157.0, 137.1 mAh/g at 0.2C and 3C rate, and capacity cycling retention rates of 97.34, 93.53% after 20 & 50 cycles, respectively.
Lithium ion battery cathode LiNi0.5Co0.2Mn0.3O2 Al2O3 coating Electrochemical performance
Kunjian Cao Li Wang Linci Li Guangchuan Liang
Institute of Power Source & Ecomaterials Science,Key Lab.For New Type of Functional Materials in Hebei Province,Hebei University of Technology,Tianjin,China
国际会议
2012 China Functional Materials Technology and Industry Forum(2012中国功能材料科技与产业高层论坛)(CFMTIF2012)
昆明
英文
235-240
2012-11-09（万方平台首次上网日期，不代表论文的发表时间）