Fatigue cracking at twin boundaries:Effects of crystallographic orientation and stacking fault energy

摘要：

　　The combined effects of crystallographic orientation and stacking fault energy (SFE) on the fatigue cracking behaviors of twin boundaries (TBs) under low cycle fatigue (LCF) tests were studied in pure Cu,Cu-Al,and Cu-Zn alloys.

关键词： twin boundaries (TB) Cu alloy fatigue cracking crystallographic orientation stacking fault energy (SFE)

作者: Zhenjun Zhang Peng Zhang Linlin Li Zhefeng Zhang