摘要：

　　The paper reports friction and wear study of TiAIN coating at different speeds and loads.The coating was deposited on YG6 (WC+6 wt.% Co) cemented carbide by cathodic arc physical vapour deposition technique.Ball-on-disc wear tests were performed on the CETR UMT-2 test system against SiC balls.The coating character and test results were obtained through SEM,XRD and Wyko surface profilometer.The results are as follows:The value of friction of coefficients decreased and depth of wear tracks became smaller as speeds and loads increased.TiAlN coating showed excellent anti-wear properties at high speed and high load,and was more suitable for these similar working conditions.

关键词： CAPVD TiAIN coating Friction Wear Wear rate

作者: Liu Aihua Liu Zeshen Zhang Peng

作者单位: Department of Mechanical Engineering, Shandong Jiaotong University,Jinan 250023, China

会议类型: 国际会议

会议名称: 2013 International Conference on Intelligent System,Applied Materials and Control Technology(GSAMCT2013)(2013年智能系统、应用材料和控制技术国际会议)

会议地点: 太原

会议语种:英文

页码: 101-104

在线出版日期: 2013-01-13（万方平台首次上网日期，不代表论文的发表时间）