Study on Melting Properties of CaO-Al2O3-SiO2-MgO System Calcium Aluminate Flux
Melting properties of CaO-Al2O3-SiO2-MgO system calcium aluminate (CA) flux were investigated through orthogonal design on three levels of four factors (content of CaO,Al2O3,SiO2 and MgO,respectively) to explore a reasonable chemical composition of CA flux.Results show that the softening temperature (Ts),hemispherical temperature (Th) and flowing temperature (Tf) of CA flux are influenced by the flux components in the order of SiO2 > MgO > CaO > Al2O3.The optimal chemical composition of flux is 3 wt.% SiO2,6~12 wt.% MgO,45 wt.% CaO and 40 wt.% Al2O3.Additionally,mineralogy composition analysis of flux clinker shows that the CA flux is mainly composed of 12CaO·7Al2O3 (C12A7),3CaO·Al2O3 (C3A) and 6CaO·4Al2O3·MgO·SiO2 (C6A4MS,Q phase).
Calcium aluminate flux melting property orthogonal experiment
Wen-ping Li Jun-hong Chen Christoph Wohrmeyer Hong-yan Guan Jia-lin Sun
School of Materials Science and Engineering, University of Science and Technology Beijing,100083 Bei School of Materials Science and Engineering, University of Science and Technology Beijing,100083 Bei Kerneos Aluminates Technologies Co.,LTD,100027 Beijing China
国际会议
北京
英文
569-572
2012-12-16（万方平台首次上网日期，不代表论文的发表时间）