Effect of foaming agent on microcellular unsaturated polyester

摘要：

　　Microcellular unsaturated polyester was prepared by different foaming agents was studied.Compared with the cell size and density of microcellular unsaturated polyester prepared using azodicarbonamide (AC),the ones of microcellular unsaturated polyester prepared using NaHCO3 were small.For NaHCO3,the cell density of microcellular unsaturated polyester decreased with the increasing temperature.For microcellular unsaturated polyester prepared using NaHCO3 at 100 ℃,the average cell size was about 18 μm and the cell density was 1.1 × 1010 celis/cm3.The compression strength at 100 ℃ is strongest among that of the materials at the other temperature.The average compression strength was 24.2 MPa.The compression strength-to-weight ratio of microcellular unsaturated polyester prepared at 90 ℃ and 100 ℃was about twice that of unsaturated polyester.

关键词： unsaturated polyester microcell cell size cell density compression strength

作者: Xueni Zhao Jianpeng He Peipei Zhai Wei Ren

作者单位: College of Mechanical and Electrical Engineering, Shaanxi University of Science and Technology,Xian Shaanxi 710021, PR China

会议类型: 国际会议

会议名称: 3rd International Conference on Frontiers of Manufacturing and Design Science(第三届制造与设计科学前沿国际会议(ICFMD))

会议地点: 香港

会议语种:英文

页码: 172-176

在线出版日期: 2012-12-11（万方平台首次上网日期，不代表论文的发表时间）