Acoustic emission monitoring for delaminated composites under bending damage failure condition
Acoustic emission (AE) was used to monitor the three point bending test of composites with a single delamination defect.The mechanical response behavior,damage and failure characteristics,and the corresponding AE characteristics of the composites have been investigated.The results show that the location of the delamination defect has little effect on the mechanical properties of the composites,whereas the damage failure mode is significantly different.The shallow delamination defect will lead to the early fracture of high-stress fibers and a large area ofdelamination propagation.As the depth of the delamination increases,the acoustic emission events decrease significantly,and the AE source location is focused on the fracture site and its adjacent areas.The AE count rate,amplitude distribution,relative energy,and source location signals are connected with the bending damage and failure of the composites.
Composites Delamination Bend Acoustic emission
Wei Zhou Xiaomin Liang Yajuan Li Shaoqing You Ruochen Liu Hanchang Chai Zhihui Lv
College of Quality and Technology Supervision, Hebei University, Baoding, China
国际会议
石家庄
英文
51-54
2012-10-26（万方平台首次上网日期，不代表论文的发表时间）