Experimental Study on Rutile TiO2 Surface Coated with Al2O3 and ZrO2
The industrial test of rutile TiO2 surface coated with Al2O3 and ZrO2 was completed using the TiO2 coated technology of low viscosity process at the TiO2 factory of PanGang group.The viscosity during the coating process,sample elements and dements distribution were respectively measured by viscometer,XRF and EDS.The results show that the viscosity of coating process is obviously lower than viscosity of existing coating technology,sample element distribution is more uniform on TiO2 surface,and the deposition rate of coating reagent is higher than it of sample using existing coating technology.The Al2O3 content fluctuation value of sample and sample using existing coating technology is respectively 0.56%,1.19% on sample surface different points,and the Al2O3 deposition rate is 93%,84.17%,respectively.
Coating TiO2 Viscosity Uniformity Deposition rate
Zhiqiang Luo Xinhong Chen Li Li
PanGang Group Research Institute Co., Ltd., State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Panzhihua, Sichuan, 617000, china
国际会议
昆明
英文
387-390
2012-10-12（万方平台首次上网日期，不代表论文的发表时间）