Polyamide 6/Polyurethane/Graphite Composites Prepared by Anionic Polymerization Process.Ⅰ. Mechanical Properties

摘要：

　　Polyamide 6/polyurethane/graphite composites have been prepared by anionic polymerization process.The effect of graphite concentration on mechanical properties of the composites was investigated.The test results show that with increment of graphite content,tensile strength of the composites increases firstly,and then decreases,while notch impact strength decreases.The change of mechanical properties of the composites is attributed to the dispersion of graphite,the interfacial properties between the matrix and graphite and the nucleation effect of graphite.In addition,the relationships between loss factor(Tan δ),storage module(E) and temperature were investigated using Dynamic Mechanical Analysis(DMTA),and the morphological characteristic of the composites were studied using Scanning Electronic Microscope (SEM).

关键词： Polyamide 6 Polyurethane Graphite Composites Mechanical Properties

作者: Xin Deng Du-Xin Li Jin Wang Jun Yang

作者单位: School of Materials Science and Engineering, Central South University of Forestry and Technology,Cha State Key Laboratory of Powder Metallurgy, Central South University, Changsha, PR China Zhuzhou Times New Material Technology Co.Ltd., Zhuzhou, PR China

会议类型: 国际会议

会议名称: 2012 2nd international Conference on Materials Science and Information Technology(2012第二届材料科学与信息技术国际会议)(MSIT2012)

会议地点: 西安

会议语种:英文

页码: 40-44

在线出版日期: 2012-08-24（万方平台首次上网日期，不代表论文的发表时间）