Fundamental Research of Sintering Process and Properties of Iron Base Composites
We have successfully synthesized iron base composites reinforced with SiC particles by a dynamic hot-pressing sintering process heating directly by electrical current.The corresponding equipment was improved and the best processing parameters was achieved after a systematically investigation.It was found that the novel sintering process,heating using continuous electrical current and then followed by dynamic temperature preservation using cyclic current,could effectively reduce the sintering time to 300 seconds and greatly improve the properties of the composites.The ultimate tensile strength of the as-prepared SiCp/Fe composite reaches 918Mpa,with a relative density of 99.8% and a hardness of 480HB.
iron base composite particle reinforced composite hot-pressing sintering mechanical properties
Yufang Yang WenBo Liu Qiang Mu
Polytechnic School of Shenyang Ligong University, Fushun 113122, China AVIC S H E NYANG AIRCRAFT CORPORATION, Shenyang 200131, China
国际会议
西安
英文
74-77
2012-08-24（万方平台首次上网日期，不代表论文的发表时间）