Woodceramics Prepared form Liquefaction Wood and Wood Powder

摘要：

　　A woodceramics makes from liquefaction wood and wood powder, the basic property connects with sintering temperature and liquefaction wood content.Thermo gravimetric analysis indicates that higher liquefaction wood content lead to reduce the weight loss.Scanning electron microscopy observation shows that wood powder is as a natural plant template and the basic structure of wood can partly keep.The apparent density increases before about 1100℃, and then decreases as temperature gets further; but the apparent porosity increases continuous; bending strength increases from 8.45 MPa to 11.87 MPa when the liquefaction wood content raises 60%-120%.Meanwhile, elevation of liquefaction wood content and sintering temperature can reduce abrasion loss.

关键词： woodceramics liquefaction wood characterization

作者: Sun Delin Yu Xianchun Sun Debin Wang Rong

作者单位: Central South University of Forestry and Technology,Changsha,Hunan,410004,China Yueyang Vocational & Technical College,Yueyan,Hunan 414000,China

会议类型: 国际会议

会议名称: the 3nd International Conference on Digital Manufacturing & Automation (第三届数字制造与自动化国际会议(ICDMA 2012))

会议地点: 桂林

会议语种:英文

页码: 585-589

在线出版日期: 2012-08-01（万方平台首次上网日期，不代表论文的发表时间）