Effect of Si on AA5182 Strip Cast by A High Speed Twin Roll Caster

摘要：

　　High speed roll casting of AA5182 aluminum alloy was tried using a vertical type high speed twin roll caster equipped with mild-steel rolls.Parting material was not used and speed was 80m/min.AA5182 strip,which thickness was 2.1 mm,could be cast continuously.However,porosity occurred at center area at the thickness direction of the strip of the as-cast strip.Si was added to original AA5182 to improve the porosity at 0.2,0.4,0.6,0.8 and 1.0 mass%.The porosity was improved as the content of the Si increased.The elongation resulting from the tension test was the best when 0.2mass%Si was added.The clack on the surface was improved by the increase of the Si content.Roll casting ability was improved by the Si,too.

关键词： twin roll caster roll casting AA5182

作者: Toshio Haga Kosuke Komeda Kenta Mtsuoka Shinji Kumai Hisaki Watari

作者单位: Osaka Institute of Technology, 5-16-1Omiya Asahiku Osaka city 535-8585, Japan Graduate school of Osaka Institute of Technology, Japan Student of Osaka Institute of Technology, Japan Tokyo institute of Technology, 4259 Nagatsuda Midoriku Yokohama city 226-8502, Japan Gunma University, 1-5-1 tenjin cho Kiryu city 376-8515 ,Japan

会议类型: 国际会议

会议名称: the 2012 International Conference on Frontiers of Mechanical Engineering and Materials Engineering (机械工程与材料工程国际会议())

会议地点: 香港

会议语种:英文

页码: 834-837

在线出版日期: 2012-07-27（万方平台首次上网日期，不代表论文的发表时间）