Manufacturing Technique of the Biocompatible Polymer Nanofiber Membrane by Electrospinning

摘要：

　　This research produced nanofiber membrane with polyethylene oxide (PEO) by electrospinning; the influence of the three parameters —mixture ratio of solution,electric field,and distance between the capillary tip and the collecting plate,on electrospinning was then explored.According to the results of the experiment,the fiber membrane with a diameter of 120 nm could be obtained when the optimum electric filed was 0.6 kV/cm and the distance between the capillary tip and the collecting board was 15 cm.Finally,the spunlace nonwoven was coated with the electrospinning solution with the optimum parameters,creating the asymmetric dressings.

关键词： electrospinning nanofiber PEO chitosan

作者: Jia-Horng Lin Jin-Jia Hu Chao-Tsang LU Wen-Cheng Chen Chien-Lin Huang Ching-Wen Lou

作者单位: Laboratory of Fiber Application and Manufacturing, Department of Fiber and Composite Materials,Feng Department of Biomedical Engineering, National Cheng Kung, University Taiwan, R.O.C. Institute of Life Sciences, Central Taiwan University of Science and Technology, Taichung 406,Taiwan Advanced Medical Devices and Composite Laboratory, Department of Fiber and Composite Materials, Feng Department of Fiber and Composite Materials, Feng Chia University, Taichung City 407, Taiwan,R.O.C Institute of Biomedical Engineering and Material Science, Central Taiwan University of Science and T

会议类型: 国际会议

会议名称: the 2012 International Conference on Frontiers of Mechanical Engineering and Materials Engineering (机械工程与材料工程国际会议())

会议地点: 香港

会议语种:英文

页码: 1404-1407

在线出版日期: 2012-07-27（万方平台首次上网日期，不代表论文的发表时间）