Effects of technical parameters on process stability and microstructure during continuous rheo-extrusion process of 6201 alloy wire

摘要：

　　In this paper,effects of technical parameters on process stability and microstructure during continuous rheo-extrusion process of 6201 alloy wire were investigated.The optimal process parameters for producing 6201 alloy wire are obtained.The casting temperature is from 720℃ to 740℃,and the roll rotating speed is 15r/min.The 6201 alloy wire with good performance has been successfully manufactured.After heat treatment,the tensile strength of the product reaches 325 MPa and the resistivity reaches 32.47 nΩm,which is better than LHA2 conducting wire of China.

关键词： Semisolid Rheo-extrusion Parameter Microstructre

作者: Renguo Guan Zhanyong Zhao Chao Lian Runze Chao Chunming Liu

作者单位: College of Materials and Metallurgy,Northeastern University,Shenyang 110004,China

会议类型: 国际会议

会议名称: the 2012 2nd International Conference on Frontiers of Manufacturing Science and Measuring Technology (第二届制造科学与检测技术国际会议(ICFMM 2012))

会议地点: 西安

会议语种:英文

页码: 219-222

在线出版日期: 2012-06-12（万方平台首次上网日期，不代表论文的发表时间）