Effect of glass fiber modification on tensile strength and shrinkage of ceramic mould
Aiming to improve the crack-resistance of the mould of ceramic mould casting,glass fibers whose average diameter was approximately 16 μm,length lmm were dispersed,and the effect of the glass fibers on the tensile strength and shrinkage rate of the ceramic mould was investigated in this study.In the ceramic green body,quartz sand was selected as refractory,silica sol was binder.The results show that,with increasing glass fiber,the tensile strength of the ceramic mould increased linearly from 0.175 MPa to 0.221 MPa at the same sintering temperature,and the shrinkage rate fell from 1.37% to 1.33% at room temperature.With the sintering temperature rising,the tensile strength increased and the shrinkage decreased by the glass fiber dispersion,but their variation rule were not changed.The investigation proposed a new method to improve the crack-resistance of the ceramic mould,i.e.,glass fiber dispersion into the ceramic mould.
Ceramic mould casting Glass fiber Tensile strength Shrinkage rate
Zhao Wang Dehong Lu Hui Gong Xiaogang He
College of Materials Science and Engineering, Kunming University of Science and Technology, Kunming, Yunnan, 650093, China
国际会议
厦门
英文
909-912
2012-01-04（万方平台首次上网日期，不代表论文的发表时间）