Wear properties of anode oxidation coating in the surface of ZL101 aluminium alloy
The oxidation film was prepared by anode oxidation method on ZL101 aluminium surface,its morphologies,compositions and phases were characterized with SEM (Scanning Electron Microscope),optical profiler,EDS (Energy Disperse Spectroscopy),respectively,its friction coefficient and abrasion performance were analyzed by wear test,and its wear mechanism was discussed.The results show that the thickness of anode oxidation layer is about 35-40μm,under dry friction condition,sliding friction coefficient is 0.65-0.72,the wear forms are abrasive attrition and adhesion wear,the low friction pair between furrows effect and adhesion effect improves the wear performance of anode oxidation film on ZL101 aluminum alloy surface.
ZL101 aluminium alloy Anode oxidation coating Friction coefficient Wear property
Wang Zhiping Yuan Feng
Department of mechanical engineering, Changzhou Institute of Light Industry Technology,Changzhou 213 Digital Design Key Laboratory of Changzhou City, Changzhou 213164, P.R.China
国际会议
昆明
英文
499-502
2011-12-28（万方平台首次上网日期，不代表论文的发表时间）