Microstructure Characterization of Rapid Solidification Al Alloy Foil

摘要：

　　The AlMn and AlMnSi foils were fabricated by rapid solidification technology.The phase transformation temperatures,microstructures and distribution of elements were characterized by Differential Scanning Calorimetry (DSC),Transmission Electron Microscope (TEM),X-ray Diffraction (XRD) and Energy Disperse Spectroscopy (EDS) respectively.The result shows that the phases of AlMn7 nanofoil conclude Al,Al6Mn and quasicrystal phase,the crystal size is about 120nm; the phases of AlMn5Si5 nanofoil conclude Al,Al4.01MnSi0.74 and Al9Mn3Si,the crystal size is about 60nm.The phase transformation temperatures of AlMn7 and AlMn5Si5 nanofoils are 543K and over 873K,respectively.The microstructure morphology of AlMn7 nanofoil are rod,block and petal-like,but the microstructure morphology of AlMn5Si5 nanofoil is homogeneous globular.

关键词： AlMn7 AlMn5Si5 foil rapid solidification microstructure

作者: Yan Li Chuanxin Zhai Chunhua Xu

作者单位: School of Mat.Sci.& Eng.,Henan University of Science and Technology,Luoyang 471003,CHINA Henan Key Laboratory of Advanced Non-ferrous Metals,Luoyang 471003,CHINA

会议类型: 国际会议

会议名称: the international conference on Frontier of Nanoscience and Technology (2011纳米科学与技术国际会议(ICFNST 2011))

会议地点: 大理

会议语种:英文

页码: 847-850

在线出版日期: 2011-08-18（万方平台首次上网日期，不代表论文的发表时间）