Properties of TiN coating prepared on 3Cr2W8V by electron beam surface alloying process
TiN coating was deposited on 3Cr2W8V alloy by PVD and then processed with electron beam surface alloying process.The microstructure,microhardness,friction coefficient,amount of wear and corrosion resistance of electron beam treated specimens were investigated.It is shown that the electron beam treated specimens can improve the properties of material.The coating has an average microhardness of approximately HV800,the friction coefficient of electron beam irradiation treated specimens is considerably lower than that of TiN coating.When the electron beam irradiate times is appropriate,the roughness of surface will much lower,and it will achieve polishing effects.The corrosion behavior of the composite coating in 3.5% Nacl solution at room temperature was also determined using a potentiont state system.In comparion with the corrosion potential for 3Cr2W8V alloy,the corrosion potentials of TiN coating and electron beam treated specimen are increased respectively.The electron beam treated specimen has the lowest corrosion current density as well as the highest corrosion potential showing an improved corrosion resistance compared with 3Cr2W8V alloy.
electron beam surface alloying microhardness wear resistance corrosion behavior
Yuan fang CHen xiao dong Peng Kang CHen Jian Jun Hu Hong bin Xu Chao Han
school of Materials Science and Engineering, Chongqing university, Chongqing ,China
国际会议
重庆
英文
698-703
2011-06-23（万方平台首次上网日期，不代表论文的发表时间）