The Preparation of Ceria-based Solid Electrolyte and the Influence of Manganese Oxide on the Performance of the Electrolyte
Ceria-based solid electrolyte was prepared by low-temperature combustion method,and the synthesis technology was discussed.It can be found that the advantages of choosing citric acid as reducing agent were higher yield and easier reaction control.The crystalline growth of samples was tended to complete when the pre-sintering temperature was 700 ℃.There was not stratification phenomenon when the forming pressure was 400 MPa.Nano-scale powders were obtained by this way,which caused decreasing of sintering temperature.The effects of Ce0.8Gd0.2O2-δ (CGO) doped manganese oxide as sintering additive on density and conductivity were studied.The relative density of CGO doped 2.0 mol% MnOi.333 (2Mn-CGO) increased within a certain temperature range because of the occurrence of viscous flow sintering.The conductivity measured at 700 ℃ of 2Mn-CGO sintered at 1100 ℃ was 4.52× 10-2 S/cm,which is higher than that of CGO.
Gadolinia-doped ceria Manganese oxide Synthesis Relative density Conductivity
Zhijuan Zhang
Research Center for Strategic Science and Technology Issues, Institute of Scientific and Technical Information of China, Beijing, 100038 China
国际会议
广州
英文
190-195
2012-11-16（万方平台首次上网日期，不代表论文的发表时间）