Effect of Spinel Content on the Oxidation Resistance Property of Magnesia-Spinel-Aluminum Composite Refractory Material

摘要：

　　Unfired specimens were made with different spinel content (5%,10%,15%,20%,25%) respectively,using high pure magnesia,magnesia-alumina spinel and aluminium as the main raw material.Unfired specimens were treated under the condition:110℃×24h drying,then 300℃×6h heating treatment.All the specimens were divided into 4 groups,and each group had five specimens from different formula.These 4 groups were treated under the temperature of 700℃,1000℃,1300℃,1600℃for heating treatment in five hours respectively.The oxidation resistance of the specimens were analyzed by XRD.The result shows that the addition of aluminium improves cold crushing strength of specimens,reaching to 58Mpa at least.The content of unoxidized aluminium is rising with the increasing of temperature for each formula.The specimen with spinel content of 25% shown the best oxidation resistance at 1600℃.

作者: MA Guodong LI Yong GAO Yuan LI Jinbao HONG Shanshan LIU Yaqin ZHANG Junjie

作者单位: University of science and technology of beijing, Beijing, China

会议类型: 国际会议

会议名称: The 6th International Symposium on Refractories (第六届国际耐火材料会议)

会议地点: 郑州

会议语种:英文

页码: 176-178

在线出版日期: 2012-10-18（万方平台首次上网日期，不代表论文的发表时间）