Effect of Pre-recovery on Recrystallization Texture in Nickel Substrates for Coated Conductors

摘要：

　　Electron backscattered diffraction (EBSD) technology was applied to study the effect of pre-recovery on the recrystallization texture in nickel substrates for coated conductors.Pure nickel (99.999%) was cold rolled by a 95% total reduction,and then samples were annealed at 200 ℃ for 1hour and quenched for fully recovery,and finally annealed at 600 ℃ for 1 hour and quenched in water.The results show that pre-recovery had a strong influence on the formation of cube recrystallization texture.Compared with samples without pre-recovery treatment at 200 ℃,samples through pre-recovery treatment can achieve stronger cube texture after recrystallization annealing,and develop more low-angle grain boundaries but less sigma 3 (∑3) grain boundaries.

关键词： EBSD pre-recovery recrystallization cube texture coated conductor

作者: Xingpin Chen Xue Chen Jingpeng Zhang

作者单位: College of Materials Science and Engineering,Chongqing University,Chongqing,400030,China

会议类型: 国际会议

会议名称: 2012 Workshop on Inorganic Thin Films and Coatings (2012年无机薄膜与涂层学术研讨会)

会议地点: 桂林

会议语种:英文

页码: 274-278

在线出版日期: 2012-07-16（万方平台首次上网日期，不代表论文的发表时间）