Fabrication and Properties of Al-Cr Coatings on the Inner Wall of Steel Pipe by Mechanical Alloying Method
The mechanical alloying method process has been innovatively used to prepare Al-Cr coating on the inner wall of steel pipe.The coating thickness was measured from all samples using optical and Scanning Electron Microscope was used to observe the surface microstructure of Al-Cr coating.Microhardness was analyzed by Digital Microhardness Tester.A wear test was performed by high speed reciprocating friction testing machine.The results show that the coating thickness is 20μm and 26μm at the rotating speed of 200 rpm and 300 rpm,respectively.The surface morphology is significantly influenced by the rotating speed.When the rotating speed was 200 rpm,a heterogeneous coating surface consisting of flattened particles produced by cold welding with less interparticle contact is formed.When the rotating speed was 300 rpm,the coating became denser and a smooth,highly consolidated and dense coating is formed.The hardness of the Al-Cr coating prepared at 200 and 300 rpm are about 250 Hv and 270 Hv.The friction coefficient of the AI-Cr coating prepared at 200 rpm are about 0.37,0.39 and 0.24 at the frequencies of 3,4 and 5 Hz.The friction coefficient of the Al-Cr coating prepared at 300 rpm are about 0.3,0.18 and 0.28 at the frequencies of 3,4 and 5 Hz.
Surface coatings Mechanical alloying Microstructure Tribological properties
Zhongqing Tian Guoxing Zhang Weijiu Huang Yukai Zhu
School of Materials Science and Engineering,Chongqing University of Technology,69 Hongguangdadao Road,Chongqing 400054,P.R.China
国际会议
2012 Workshop on Inorganic Thin Films and Coatings (2012年无机薄膜与涂层学术研讨会)
桂林
英文
279-282
2012-07-16（万方平台首次上网日期，不代表论文的发表时间）