Synthesis and Characterization of Bi2Al4O9 Powders
Bi2Al4O9 powders were prepared by sol-gel process.The precursors were heated at 500-800℃ for 2h to obtain Bi2Al4O9 powder and X-ray diffraction (XRD),Differential thermal analysis (DTA),thermogravimetric analysis (TG),field emission scanning electron microscope (SEM),Fourier transform infrared spectroscopy (FT-IR) techniques were used to characterize precursor and derived oxide powders.XRD analysis show that the powder is still amorphous after calcined at 500℃.The peaks of Bi2Al4O9 become sharp after calcined at 575℃ though still existing some amorphous phase.After calcining at 675-800℃,the powder has fully turned into pure Bi2Al4O9 phase.The crystallization process can also be confirmed by DTA-TG and IR.Calcining the precursor at 575℃,the absorption bands at 527 cm-1,738 cm-1,777 cm-1,and 919 cm1are observed,which are assigned to Bi2Al4O9 and becoming stronger and sharper with the increase of temperature.
sol-gel process Bi2Al4O9 powder synthesis characterization
Xiaoyan Zhang Wenshu Hu Xiwei Qi Guifang Sun Jianquan Qi Huanhuan Chen Ruixia Zhong
School of Resources and Materials,Northeastern University at QinHuangDao Branch,QinHuangDao 066004
国际会议
桂林
英文
34-37
2012-07-16（万方平台首次上网日期，不代表论文的发表时间）