Evolution of micro-orientations on Non-oriented Silicon Steels during the annealing process based on the CSP

  In this paper,studied was the low carbon and low silicon (0.003%C,0.3%Si)cold-rolling steel sheet whose reduction ratio was 81% annealed at 870 ℃ in the laboratory salt-bath furnace and heated for 180s.The evolution of micro-orientations of grain coarsening at 1050℃ and 1150℃ on cold-rolling samples that were annealed at temperature 870℃ and heated for 180s was studied by EBSD technology.

Non-oriented Silicon Steel annealing EBSD texture

Zili Jin Wei Li Lizhen Guo

Inner Mongolia University of Science and Technology Institute for Materials and Metallurgy Baotou 01 Baotou Iron & Steel(Group)Co., Ltd., making steel plant ,Baotou 014010, China