Three-Body Abrasive Wear Behavior of Basalt and Glass Fabric Reinforced Epoxy Composites

摘要：

　　Three-body abrasive wear behavior of basalt-epoxy (B-E) and glass-epoxy (G-E) composites have been investigated using Dry sand rubber wheel abrasion resistance for various abrading distance,viz.,150,300,450 and 600m and different loads(22N and 32N) at 200 rpm.The weight loss and specific wear rate as a function of load and abrading distance were determined.The weight loss increases with increasing load and also with abrading distance while the specific wear rate decreases with increase in abrading distance and increases with the load.Better abrasion wear resistance was observed in B-E composite compared to G-E composite.Scanning Electron Microscope (SEM) is used to examine the abraded composite specimens and revealed that the more damage occur to glass fiber compared to basalt fiber.Also good interfacial adhesion was observed between epoxy and basalt fiber which leads to good abrasive wear resistance.

关键词： Basalt-epoxy composite Glass-epoxy composite Three-body abrasive wear Worn surface morphology, mechanical properties

作者: C.Anand chairman S.P.Kumaresh Babu

作者单位: Department of Metallurgical and Materials Engineering, National Institute of Technology-Tiruchirappalli, India

会议类型: 国际会议

会议名称: the Second International Conference on Frontiers of Manufacturing and Design Science(第二届制造与设计科学国际会议(ICFMD 2011))

会议地点: 台湾

会议语种:英文

页码: 534-538

在线出版日期: 2011-12-11（万方平台首次上网日期，不代表论文的发表时间）