Properties of BiFeO3 Thin Films Prepared with Self-assembled Monolayers by Liquid Phase Deposition
Using iron nitrate,bismuth nitrate,citric acid and glacial acetic acid as the raw materials,the BiFeO3 thin films in crystalline state were prepared on FTO substrate with the self-assembled monolayers by liquid phase deposition after graded induction and annealing at 550 ℃ for 30 min.The physical phase composition,the surface morphology and dielectric properties of the thin films were characterized respectively by XRD,SEM,and Precision LCR Meter.This paper studied that the deposition temperature and the number of film layers had the effects on the thin films.The results show that the as-prepared thin films show the random orientation and good crystalline.When the deposition temperature is 70 ℃,the surface of the as-prepared thin film is smooth and uniform.The size of grain is 100 nm.The thin film has a dense structure without the apparent pore phase.When the test frequency is between 1kHz and 1MHz,the loss of the thin films is decreased as the increase of the number of the film layers.When the number of the layers is 15,the dielectric constant of the thin films is 44 and the loss is 0.02 when the test frequency is 10 kHz.
BiFeO3 thin film Self-assembled monolayers Dielectric properties
Jun Yin Guoqiang Tan Lihua Song Ao Xia Huijun Ren
School of Material Science & Engineering,Shaanxi University of Science & Technology,Xian 710021,China
国际会议
The Seventh China International Conference on High-Performance Ceramics (第七届先进陶瓷国际研讨会(CICC-7))
厦门
英文
1244-1248
2011-11-04（万方平台首次上网日期，不代表论文的发表时间）