Piezoelectric and Strain Properties of Strontium-Doped BZT-BCT Lead-Free Ceramics
Lead-free piezoelectric ceramics,(Ba0.85-xSrxCa0.15)(Zr0.1Ti0.9)O3 (BSCZT,x=0.01-0.07),were prepared via a solid-state reaction route.The dielectric properties,ferroelectric properties,piezoelectric and strain properties of BSCZT ceramics were studied.The phase structure and microstructure were investigated by X-ray diffraction and scanning electron microscope,respectively.Results showed that dense ceramics with pure perovskite phase were obtained.At room temperature,the samples with x=0.03 exhibited excellent properties with large piezoelectric coefficient d33=534pC/N,planar mode electromechanical coupling coefficient kp=47.7%,thickness mode electromechanical coupling coefficient kt=42% and high strain levels of 0.34%.In addition,the study of electrical properties suggested that the Curie temperature decreased linearly from 92(℃) to 73(℃) with the increasing doping content of strontium in BCZT ceramics.The remnant polarizations,piezoelectric coefficient and strain levels were all increased as the Sr content increased and then decreased with further increased Sr doping level,giving the maximum values at the Sr content of 3mol%.These results indicated that the BSCZT system is a promising lead-free material for applications in the future.
Lead-free ceramics Piezoelectric properties BaTiO3
Wangfeng Bai Wei Li Bo Shen Jiwei Zhai
Functional Materials Research Laboratory,Tongji University,Siping Road,Shanghai 200092,China
国际会议
The Seventh China International Conference on High-Performance Ceramics (第七届先进陶瓷国际研讨会(CICC-7))
厦门
英文
1385-1389
2011-11-04（万方平台首次上网日期，不代表论文的发表时间）