Preparation and Characterization of Anti-oxidation Coatings for Sliding Plates
High-temperature anti-oxidation coating was prepared by a milling process,which mainly composed of flake graphite and hexagonal BN (hBN).The coating was brushed on the sliding plate surface and dried in air for 24 h,The surface of the sliding plate painted was smooth and without peeling,suggesting a strong bonding strength.The samples were heated at 1200 ℃ for 20 min to evaluate the mass-loss rate.The mass-loss rate of the slide gate painted is 3.7%,less than the un-painted 5.1%.XRD and SEM techniques were used to characterize the as-heated samples.The results showed that the surface of the slide plate painted was skin rolling.And the graphite reacted with oxygen at an elevated temperature to reduce oxygen concentration.In addition,hBN also reacted with oxygen to form B2O3,which also has an oxygen-resistant role in the sliding plates.These coatings exhibited unique oxidation-resistant properties,and the service life of the coated sliding plates was obviously improved.
Anti-oxidation coating slide plate service life
Lina Wang Bingbing Fan Rui Zhang Hailong Wang Deliang Chen
School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001, China School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001, China;Zhengzhou
国际会议
The Sixth China International Conference on High-Performance Ceramics(第六届中国先进陶瓷国际研讨会(CICC-6))
哈尔滨
英文
432-434
2009-08-16（万方平台首次上网日期，不代表论文的发表时间）