Preparation of Rutile Crystalline Glaze
Crystalline glaze is a kind of art glaze with excellent decorative performance,the existing crystalline glaze mainly willemite crystalline glaze,systems on a single track.In this paper,the use of crystalline glaze raw materials for glass,ZnO and coke gemstones,CuO as coloring agents,using orthogonal to determine the formula,this paper researched that added TiO2 to the willemite crystalline glaze crystal phase composition as well as the amount of TiO2 and processing conditions on the preparation of crystalline glaze crystal flower morphology impact.The results show that under the conditions of 1250℃ melting 1130℃ crystallization process crystal spontaneous growth in crystalline glaze can be able to cover the entire glazed,shape of crystals was feathered,cross growth,the number of crystal increased with crystallization temperature,glaze was smooth and shiny sense.XRD and optical microscopy analysis showed that the precipitation of crystals was the long column of futile,crystal distributed equality,under a polarizing microscope in purple,green and black,with strong aesthetic values.
Rutile Crystalline Glaze Crystal flower morphology
Xia Yinfeng Huang Zhaohui Yuan Jiazheng Wang Linjun Xie Jiehua
Technolgy Center of Beijing Tongda Refractory Technologies Co., Ltd, Beijing 100085, China China University of Geosciences, Beijing 100083, China
国际会议
The Sixth China International Conference on High-Performance Ceramics(第六届中国先进陶瓷国际研讨会(CICC-6))
哈尔滨
英文
778-781
2009-08-16（万方平台首次上网日期，不代表论文的发表时间）