A Promising LaSmZr2O7 Ceramic with Pyrochlore Structure for Thermal Barrier Coatings
Based on La2Zr2O7 ceramic for thermal barrier coatings,LaSmZr2O7 ceramic doped with samarium ion was successfully prepared using solid state reaction method.The pellets were sintered at 1600℃ for 10 hours in air.The phase structure,thermal conductivity and thermal expansion coefficient of LaSmZr2O7 ceramic and La2Zr2O7 ceramic were measured by XRD,laser-flash device,high-temperature dilatometry,respectively.The results show that the crystal structure of LaSmZr2O7 ceramic is not affected by the doped samarium ion in the zirconium lattice.The thermophysical results showy that the thermal conductivity of the LaSmZr2O7 ceramic is lower than that of La2Zr2O7 ceramic,while the thermal expansion coefficient is higher than that of La2Zr2O7 ceramic.These results indicate that LaSmZr2O7 ceramic or Ln2Zr2O7 ceramics doped with other rare earth ions could be candidate materials for future thermal barrier coatings.
La2Zr2O7 ceramic Samarium ion Thermal conductivity Thermal expansion
Xu Qiang Pan Wei Wan Chunlei Qi Longhao Miao Hezhuo Wang Fuchi
School of Materials Science and Engineering,Beijing Institute of Technology,Beijing 100081,China State Key Laboratory of New Ceramics and Fine Processing,Department of Materials Science and Enginee
国际会议
The Fifth China International Conference on High-Performance Ceramics (第五届先进陶瓷国际研讨会(CICC-5))
长沙
英文
1328-1330
2007-05-10（万方平台首次上网日期，不代表论文的发表时间）