Utilization of Blast Furnace Slag, Steel Slag in the Production of Clinker
The study on the use of blast furnace slag,steel slag and fly ash as raw materials to produce cement clinker has been carried out in the present investigation.The burnability of raw meal was determined by the linear shrinkage and free lime content of clinkers sintered at different temperatures.The microstructrue and properties of raw meal and clinker were investigated by the means of chemical analysis,X-ray diffraction and petrographic analysis.The physical and mechanical performance of cement was tested according to the standards.The results showed that the burnability was good as the free lime content was lower than 0.5w% in the clinker sintered at 1350℃.It is believed that the nucleation of alite only needs to grow bigger and rearrange with the rising temperature.The micrograph of clinker sintered at 1450℃ showed that there were some garlands of belite crystals around alite crystals because of high temperature or the local reducing atmosphere caused by the compact raw meal.High-quality cement clinker with compressive strength of 60.4MPa was produced by utilizing limestone,blast furnace slag,steel slag and fly ash as raw materials after curing 28 days.
Clinker Blast furnace slag Steel slag Burnablity Performance
Shouwan Qin Jianjun Shen Huifen Wang Zhaoran Xiao
Henan University of Technology, Zhengzhou, 450052, China Construction Project Quality Supervision Station of Zhengzhou City, Zhengzhou, 450000, China
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
334-338
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）