High Quality MgB2/Nb Deposited by HPCVD Method
Niobium with the transition temperature of 9 K is the usual material for TESLA superconducting accelerate cavity.The cavity must work at the temperature range of of 2~1.8 K,which would consume large energy.In addition,the low upper critical field is one of reasons causing the problem of accelerate cavities Q-slop.Comparing with Nb material,MgB2 has several advantages in this application,such as higher Tc of ~39 K,higher upper critical field and the possible lower microwave loss,which would help increasing accelerating gradient and saving operation cost.Because of these benefit,more and more focus is put on this style of accelerating cavity,MgB2-thick-film/metal-cavity-body.Using Hybrid Physical-Chemical Vapor Deposition method,the micronmeter-thick MgB2 film on Nb substrate was prepared in the present investigation.The experimental results showed that Tc(0) reached 38.5 K and the Hc2 was about 20 T.In order to test the films fracture toughness the film as the inner surface was bended.It was found that at small bending angle the influence on the superconducting properties was little.When the bend radius increased to 5 mm,some cracks smaller than 1 micron occured on the film surface.However,the film still attached to the Nb substrate and the Tc was as high as ~33.5 K,showing that the MgB2 film fabricated by HPCVD had a good compact state with the Nb substrate and good mechanical toughness.These results indicate that the clean MgB2 thick film has a better feature in the application of superconducting accelerate cavity.
MgB2 Superconducting accelerator
Liping Chen Fa He Chen Zhang Yan Zhang Yiling Chen Qingrong Feng Zizhao Gan
Physics department, Zhejiang Normal University, Jinhua 321004, China School of Physics and State Key Laboratory of Nuclear Physics and Technology, Peking University,Beij Physics department, Peking University, Beijing 100871, China
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
203-207
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）