Preparation of EuBCO Epitaxial and Textured Films By F-Free Polymer-assisted Chemical Solution Deposition Method

  Epitaxial and textured EuBa2Cu3O7-x(EuBCO) superconductive films were prepared via a F-free polymer-assisted chemical solution deposition (PACSD) method on LaAlO3 (LAO) single crystal substrate in nitrogen atmosphere.Because of the fluorine-free metal organic system,no harmful gas was produced during processing by the PA-CSD method.The film morphorlogy,phase composition,texture and the superconducting critical temperature (Tc) of EuBCO films were investigated by x-ray diffraction(XRD),φ-scan,ω-scan rocking curves,an environmental scanning electron microscope(ESEM) and four-probe method.The Jc value of the EuBCO film in self-field at 77K was measured by using Jc-scan Leipzig system.The results shoed that a denser microstructure and better biaxial texture EuBCO film after a high temperature treatment with a superconducting critical temperature (Tc) of 91K was obtained.The critical current density (Jc) reached 2.4MA/cm2 at 77K in the self-field.

Fluorite-free PACSD EuBCO High temperature heat treatment

Xin Zhang Cuihua Cheng Wentao Wang Yong Zhang Yong Zhao

Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China School of Materials Science and Engineering, University of New South Wales, Sydney, 2052,NSW, Austra Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China

国际会议

the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))

太原

英文

261-266

2012-07-13(万方平台首次上网日期,不代表论文的发表时间)