Effects of SiO2 and ZrO2 Additives on Microstructure and Properties of Al2O3 Ceramic
Alumina ceramic,with high mechanical strength,good electric insulation,high hardness and good corrosion resistance performance,has been widely used in machinery,electronic and electrical,chemical,medicine,construction and other high-tech areas.In this study,both silicon sol and zirconia particles are incorporated into the system and dense alumina composite ceramics were prepared by cold isostatic processing and pressureless sintering at 1550 ℃.The influence of additives on phase composition,microstructure and mechanical properties were investigated.The XRD results show that mullite phase was generated in the composite ceramic.The composite ceramic has excellent comprehensive performance.For example,the sample with 3wt.% SiO2 and 5wt.% ZrO2 has density of 3.87g·cm-3,Vickers hardness of 17.6GPa,flexural strength of 369.0MPa,youngs modulus of 374.2GPa and fracture toughness of 3.57MPa·m1/2.
Al2O3 SiO2 ZrO2 Composite ceramic
Yihua Li Dechang Jia Zhihua Yang Yu Zhou
Institute for Advanced Ceramics, Harbin Institute of Technology, Building C3, Science Park, Harbin Institute of Technology, No.2 Yikuang Street, Nangang District, Harbin, Heilongjiang Province,China
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
523-527
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）