Fabrication and Mechanical Properties of SiC/Cu Composites with Zn Addition by Hot Pressing Sintering
SiC/Cu composites exhibit low density,low coefficient of thermal expansion and excellent mechanical properties.In this study,Zn of 2 wt.% was added as the sintering activator,and the high volume faction (60%) SiC/Cu composites was fabricated by hot pressing sintering technology.The phase composition and morphology of as-prepare samples were characterized by X-ray diffraction (XRD) system and scanning electron microscopy (SEM) equipped with an energy-dispersive spectroscopy (EDS) system.The as-prepared SiC/Cu composites were dense and uniform as well as void free.The results show that SiC/Cu composites can reach excellent mechanical properties of SiC/Cu composites.With the increase of sintering temperature,Vickers hardness and the bending strength of the samples increased obviously and the as-prepared SiC/Cu composites achieved a maximum Vickers hardness and bending strength respectively of 195MPa and 140MPa.
SiC/Cu Composite Hot pressing sintering Mechanical properties Interface
Huang Liu Guoqiang Luo Pingan Chen Qiang Shen Qiang Shen
State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Tec State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Tec
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
700-705
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）