Fabrication of Zr55Al10Ni5Cu30 Amorphous Composite Coating on Plain Carbon Steel by Laser Cladding and Remelting
A Zr-based amorphous composite coating was fabricated by laser cladding and remelting on plain carbon steel.The amorphous phase contents of coatings were tailored by controlling the power density.The effect of amorphous phase content along the depth direction on the microhardness and corrosion resistance of the coating was studied.The results showed that the content of amorphous phase significantly decreased from the remelted layer to the cladded layer.In addition,it was found that the maximum microhardness of the coating were about 1061 HV0.1,observed 200 μm beneath the surface.Potentiodynamic polarization studies in 3.56 wt.% NaCl solution indicated that the remelted layer exhibited excellent corrosion resistance due to the high amount of amorphous phase.
Amorphous Laser Coating Microhardnes Corrosion resistance
Gaozhi Jia Wenxian Wang Xu Liu Zeqin Cui Bingshe Xu
College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024,China;Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education,Taiyuan 030024, China
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
746-753
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）