Experimental Research on the Friction and Wear Properties of Ni-based Composite Coating prepared by Laser Cladding

摘要：

　　In this study,the dry sliding wear behavior of Ni-based self-lubricating wear-resistant coating was characterized under various loads at 300 ℃.Morphologies and compositions of the worn surface were analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).The experimental results showed that with the increase of load,both the frictional coefficient and wear rate decreased firstly,then slightly increased.A small amount of debris dispersed on the worn surface of the coating under low load (2 N).Since the effects of oxide layer and lubricant particles spreading onto the worn surface,the coating exhibited superior friction,and improved the wear properties under moderate load (5 N).As the load further increased,till up to 10N,the worn surface started to appear some shallow grooves and craters.This was contributed to the dispersion of carbides and lubricant particles.

关键词： Self-lubricating wear-resistant coating Variation of load Friction and wear Wear mechanism analysis

作者: Shufa Chen Chenglong Feng Jin Yang Jinsong Chen

作者单位: College of Mechanical Engineering, Huaihai Institute of Technology, Lianyungang, China

会议类型: 国际会议

会议名称: the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))

会议地点: 太原

会议语种:英文

页码: 152-157

在线出版日期: 2012-07-13（万方平台首次上网日期，不代表论文的发表时间）