Dynamic Precipitation Behaviors and Mechanical Properties of Mg-12Gd-3Y-0.5Zr Alloy Processed by Secondary Extrusion
Secondary extrusion at 350 °C with the extrusion ratio of 12.25,25 and 44 was carried out on the Mg-12Gd-3Y-0.5Zr (GW123K) alloy,and the cooling method of the secondary extruded alloys was air cooling and water quenching.Quantitative metallographic analysis method was also employed to study the distribution and volume fraction of dynamic precipitates during the extrusion process.The results showed that secondary extrusion could result in significant grain refinement and the grain size increased with extrusion ratio,which the minimum average grain size was about 5.4μm in the alloy under λ=12.25.The volume fraction of dynamic precipitates decreased with increasing extrusion ratio and the maximum volume fraction was measured to be about 49.2% in the alloy under λ =12.25.Water quenching after extrusion can effectively inhibit dynamic precipitation and the volume fraction of the precipitates ratio decreased from 41.1% after air cooling to 19.6% after water quenching in the same extrusion condition.Tensile properties results showed that the age hardening response of the alloys was decreased by dynamic precipitation and water quenching was an efficient method which is able to avoid this behavior in some extent.
Mg-Gd-Y-Zr alloys Secondary extrusion Dynamic precipitation Precipitation hardening Mechanical properties
Dejiang Li Yinpeng Zhou Xiaoqin Zeng Wenjiang Ding Bin Chen Yingzheng Liu
National Engineering Research Centre of Light Alloy Net Forming, the State Key Laboratory ofMetal Ma Instrumental Analysis Center of School of Materials Science and Engineering, Shanghai Jiaotong Unive School of Mechanical Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road,Shanghai 200240,
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
192-197
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）