Effect of Rolling Reduction on Microstructure and Mechanical Properties of Mg-9Gd-3Y-0.5Zr Alloys
Rolling processing has been carried out on samples cut from the extruded Mg-9Gd-3Y- 0.5Zr seamless tubes.Effects of rolling reduction,5%,20% and 70% per pass,on its microstructure and mechanical properties were investigated.The results showed that the strength and ductility varied with increasing rolling passes at different rolling reduction.The strength of the alloy rolled by 5% reduction per pass gradually improved with increasing rolling passes,and its ductility remained basically constant.However,when 20% reduction per pass was applied,the strength and ductility of the alloy after rolling increased at first and then decreased a little after the accumulative strain higher than 52%.Moreover,as reduction reached 70% per pass,macro-cracks were induced when rolling at 420°C,while the samples were rolled at a high temperature of 500°C and a larger reduction of 70% per pass exhibited the mechanical properties comparable to those fabricated by 5% and 20% reduction.This indicated that a relatively higher productivity via rolling as well adequate mechanical properties can reach for the large scale of industrial products.
Mg-Gd-Y alloy Rolling:Reduction per pass Microstructure Mechanical properties Ageing
S.Q.Li W.N.Tang R.S.Chen E.H.Han W.Ke
State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Road, Shenyang 110016, China
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
223-229
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）