Biodegradable Behaviors in Simulated Body Fluid of Mg-Gd-Y-Zr Alloy with Micro-arc Oxide Coating
The effects of micro-arc oxidation (MAO) on corrosion resistance of Mg-Gd-Y-Zr magnesium alloy have been studied.The Mg-Gd-Y-Zr with thicker oxide coating presented higher corrosion resistance in simulated body fluid (SBF).The corrosion rates were measured by several methods including hydrogen evolution volume measurement,weight-loss method and determination of pH as an auxiliary reference.The surfaces of specimens were observed by SEM and white light confocal microscopy before and after the corrosion.Besides the effects of MAO,the pitting resulted from breakage of oxide coating played a notable role as well.This provided a new direction towards the enhancement of corrosion resistance of magnesium alloy.
Biomedical magnesium alloys Biodegradable behavior Bio-environment immersion Micro-arc oxidatio
Kaiyang Yin Tianfeng Lu Qing Dong Bingyi Sun Bin Chen
School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 20040,China
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
295-300
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）