Effects of Solid Solution Treatments on Microstructures and Tensile Properties of a Mg-Y-Zn-Cu Alloy
In this study,a Mg-2.1Y-0.5Zn-0.6Cu-0.1Zr (WZC200,in at.%) alloy was prepared by permanent casting method.On the basis of thermal analysis results during solidification process,two temperatures (T1/763K and T2/773K) were selected for subsequent solid solution treatments.Microstructure evolution and the tensile property changes after T4 treatment at T1 and T2 for different holding time were also investigated in this study.The tensile testing results showed that yield strength and ultimate tensile strength were improved with the fraction increase of the lamellae-shaped LPSO phase in the grain interiors,rather than the total fraction of LPSO phase.
Mg-Y-Zn-Cu alloy Magnesium alloy Long period stacking order (LPSO) structure Solid-solution treatment
Bingqing Shi Rongshi Chen and Wei Ke
State Key laboratory for Corrosion and Protection, Institute of Metal Research, Wencui Road 62,Sheny State Key laboratory for Corrosion and Protection, Institute of Metal Research, Wencui Road 62,Sheny
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
449-456
2012-07-13(万方平台首次上网日期,不代表论文的发表时间)