Effect of Salt-coating Hot Corrosion on Stress-rupture Properties of a Corrosion Resistant Directionally Solidified Superalloy
The hot components of gas turbine are loaded by high stresses in presence of high-temperature oxidation and hot corrosion environment during service process.It is important to simulate the interaction of stress and hot corrosion on the components in real service situation.Effect of the ratios of salt mixtures of Na2SO4/NaCl and the coating amounts of salt mixtures on the microstructure and the high temperature stress-rupture properties of a corrosion resistant directionally solidified superalloy at 850℃/500MPa were investigated.The results demonstrated that the stress-rupture life decreased with the coated salt mixture ratio of Na2SO4/NaCl changing from 3:1 to 9:1.Stress-rupture lives of the alloy decreased from 63 h to 42 h,while the coated salt mixtures amount increased from 1 mg/cm2 to 4 mg/cm2,hereby the salt mixture contained 75% Na2SO4 and 25% NaCl.When the coating ratio of Na2SO4/NaCl was 9:1,the stratified corrosion products layers were composed of the (Ni,Co)O,Ni(Al,Cr)2O4 layer,bright grey phase that be identified as CrWO4,and the underlying dispersed particle shape phase CrSx,the underlying layer forms the sulfides eutectic and leads to catastrophic destruction for the alloy,which decreased the stress-rupture lives dramatically.
Directionally solidified superalloy:Stress-rupture properties Hot corrosion Salt coating Deterioration mechanism
Xueda Chen Qing Li Chengbo Xiao Weipeng Ren
National Center for Materials Service Safety University of Science and Technology Beijing, Beijing, Science and Technology on Advanced High Temperature Structural Materials Laboratory Beijing Institut
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
502-506
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）