Superalloys and the Development of Advanced Ultra-supercritical Power Plants
A 700℃ advanced ultra-supercritical (A-USC) power plant technology project was initiated in China in the year of 2011.The highest temperature components in A-USC boiler are superheater and reheater tubes.The fire-side metal temperature can reach 750℃ (even higher).Based on the very long time service(30-40 years) these important high temperature tubes require 105h long time stress rupture strength higher than 100MPa and the corrosion/oxidation layer loss less than 2mm for 2×105h.The highest temperature components in 700℃ steam turbine are the buckets of different stages and require very long service time.At this severe condition only superalloys can fulfill these unusual requirements.This paper reviewed Fe-Ni and Ni-base superalloys from the view point of structure stability and long term mechanical properties and corrosion/oxidation resistance for 700℃ A-USC power plant materials selection.
700C A-USC power plant:Fe-Ni and Ni-base superalloys:Structure stability
Xishan Xie Chengyu Chi Shuangqun Zhao Jianxin Dong Fusheng Lin
School of Materials Science and Engineering, University of Science and Technlology Beijing,Beijing 1 School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,Bei Department of Materials and Technology, Shanghai Power Research Equipment Institute,Shanghai 200240,
国际会议
the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))
太原
英文
594-603
2012-07-13（万方平台首次上网日期，不代表论文的发表时间）