Phase Transformation Behavior and Mechanical Properties of Ti-Mo-Sn Alloys

摘要：

　　A series of Ti-Mo-Sn alloys with different Mo contents from 7%to 15% (wt.%) were prepared,and the effects of Mo content and thermo-mechanical treatment on their microstructural evolution and mechanical behavior were investigated.The experimental results indicated that the β to α martensite transformation can be effectively suppressed with increasing Mo content.After cold rolling treatment,superior mechanical properties and low modulus were achieved in Ti-8Mo-4Sn alloy,with tensile strength of 1108MPa,yield strength of 1003MPa and low Young’s modulus of 53GPa.The influence of severe cold deformation on the macrostructure and mechanical properties was discussed based on the characterization of X-Ray diffraction and mechanical tests.It was demonstrated that the cold rolling induced fine α martensite and high density dislocations lead to the high strength of the Ti-Mo-Sn alloys.The fine α martensite as well as the β matrix with low stability guarantee low Youngs modulus.

关键词： Near β titanium alloy Phase transformation Mechanical properties Modulus

作者: Xiaoxue Chen Shun Guo Xinqing Zhao

作者单位: School of materials Science and engineering, Beihang University, Beijing, 100191, China

会议类型: 国际会议

会议名称: the Chinese Materials Congress 2012(2012年中国材料大会(CMC2012))

会议地点: 太原

会议语种:英文

页码: 855-859

在线出版日期: 2012-07-13（万方平台首次上网日期，不代表论文的发表时间）